Formation of Low Acetyl Content Cellulose Acetate Membrane for CO2/N2 Separation
Main Article Content
Abstract
The rising carbon dioxide (CO2) emissions over the decades is known to be a huge contributor to the greenhouse effect. CO2 capture and storage methods have been perceived as favourable solutions to prevent global warming and climate change rising from the greenhouse effect. One energy efficient technology for separating CO2 is the development of high-performing CO2 gas separating membranes. A variety of membrane-based gas separation technologies designed have shown promising results and are inexpensive. A high-performing membrane must have a defect-free, thin dense skin-layer with a porous sub-layer for support that permits great permeation rate and selectivity. Of all ranges of polymers used to make polymeric membranes for CO2/nitrogen (N2) separation, cellulose acetate (CA) polymer membranes are known for their high CO2 solubility. In this research, the effect of CA polymer concentrations at low acetyl group of 39.8% and casting thickness on the structure and morphologies of the membranes were studied. The CA polymer concentration was optimised from a range of 10 wt%, 15 wt% and 20 wt%, and the casting thickness was optimised from a range of 150 μm to 400 μm using wet-phase inversion technique. The results obtained exhibit a CA membrane with thin dense, selective skin-layer achieved at CA polymer concentration of 15 wt% and a casting thickness of 300 μm, with a CO2 permeance rate of 401.173 ± 0.579 (GPU), N2 permeance rate of 133.499 ± 0.148 (GPU) and selectivity of 3.009 ± 0.00656. This CA membrane is able to contribute to promising gas separation performances with enhanced physical and mechanical support by improvement of membrane permeance and selectivity towards CO2/N2 separation performance.
Article Details
This work is licensed under a Creative Commons Attribution 4.0 International License.
References
Yamasaki, A. (2003). An overview of CO2 mitigation options for global warming emphasizing CO2 sequestration options. J. Chem. Eng. Jap., 36, 361–375, https://doi.org/10.1252/jcej.36.361.
Archer, D. & Brovkin, V. (2008). The millennial atmospheric lifetime of anthropogenic CO2. Clim. Change, 90, 283–297, https://doi.org/10.1007/s10584-008-9413-1.
Merkel, T. C. et al. (2010). Power plant post-combustion carbon dioxide capture: An opportunity for membranes. J. Membr. Sci., 359, 126–139, https://doi.org/10.1016/j.memsci.2009.10.041.
Harding, J. (2007). Economics of nuclear power and proliferation risks in a carbon-constrained world. Electr. J., 20, 65–76, https://doi.org/10.1016/j.tej.2007.10.012.
Favre, E. (2007). Carbon dioxide recovery from post-combustion processes: Can gas permeation membranes compete with absorption? J. Membr. Sci., 294, 50–59, https://doi.org/10.1016/j.memsci.2007.02.007.
Carapellucci, R. & Milazzo, A. (2003). Membrane systems for CO2 capture and their integration with gas turbine plants. Proc. Inst. Mech. Eng. A JPEE, 217, 505–517, http://dx.doi.org /10.1243/095765003322407557.
Powell, C. E. & Qiao, G. G. (2006). Polymeric CO2/N2 gas separation membranes for the capture of carbon dioxide from power plant flue gases. J. Membr. Sci., 279, 1–49, https://doi.org/10.1016/j.memsci.2005.12.062.
Spillman, R. & Cooley, T. (1987). Economic considerations in membrane gas separation process design. New York: AIChE.
Rajesh, S. et al. (2011). Preparation and characterisation of poly (amide-imide) incorporated cellulose acetate membranes for polymer enhanced ultrafiltration of metal ions. Chem. Eng. J., 171, 33–44, https://doi.org/10.1016/j.cej.2011.03.033.
Ngang, H. et al. (2012). Preparation of mixed-matrix membranes for micellar enhanced ultrafiltration based on response surface methodology. Desalin., 293, 7–20, https://doi.org/10.1016/j.desal.2012.02.018.
Coltelli, M. B. et al. (2008). Poly (lactic acid) properties as a consequence of poly (butylene adipate‐co‐terephthalate) blending and acetyl tributyl citrate plasticization. J. Appl. Polym. Sci., 110, 1250–1262, https://doi.org/10.1002/app.28512.
Ahmad, A. et al. (2014). A cellulose acetate/multi-walled carbon nanotube mixed matrix membrane for CO2/N2 separation. J. Membr. Sci., 451, 55–66, https://doi.org/10.1016/j.memsci.2013.09.043.
Murad, S. & Nitsche, L. C. (2004). The effect of thickness, pore size and structure of a nanomembrane on the flux and selectivity in reverse osmosis separations: A molecular dynamics study. Chem. Phys. Lett., 397, 211–215, https://doi.org/10.1016/j.cplett.2004.08.106.
Jawad, Z. et al. (2015). Incorporation of inorganic carbon nanotubes fillers into the CA polymeric matrix for improvement in CO2/N2 separation. Curr. Nanosci., 11, 69–79.
Zhang, X. R. et al. (2011). One-step fabrication and analysis of an asymmetric cellulose acetate membrane for heat and moisture recovery. J. Membr. Sci., 366, 158–165, https://doi.org/10.1016/j.memsci.2010.09.054.
Xing, D. Y., Peng, N. & Chung, T. S. (2010). Formation of cellulose acetate membranes via phase inversion using ionic liquid,[BMIM] SCN, as the solvent. Inl. Eng. Chem. Res., 49, 8761–8769, https://doi.org/10.1021/ie1007085.
Sofiah, H., Nora’aini, A. & Marinah, M. (2010). The influence of polymer concentration on performance and morphology of asymmetric ultrafiltration membrane for lysozyme separation. J. Appl. Polym. Sci., 10, 3325–3330.
Ahmad, A., Low, S. & Shukor, S. A. (2007). Effects of membrane cast thickness on controlling the macrovoid structure in lateral flow nitrocellulose membrane and determination of its characteristics. Scr. Mater, 57, 743–746, https://doi.org/10.1016/j.scriptamat.2007.06.037.